Potential of Avocado Seed Extract (Pasea Americana) As A Corrosion Inhibitor Against Surface Roughness OF CUNITI Orthodontic WIRE
Abstract
The surface roughness of orthodontic archwires is an essential factor that deter- mines the effectiveness of arch-guided tooth movement. CuNiTi-based wires are widely used in orthodontic treatment, but the oral environment can trigger corrosion of CuNiTi orthodontic wires. The tannin content in avocado seed extract can be used as a corrosion inhibitor through two working mechanisms, namely, forming a passive layer and an adsorption process. The aim of this research is to examine the effect of avocado seed extract as a corrosion inhibitor on the surface roughness of orthodontic CuNiTi wire. The as- retacngular 17 x 25 inch CuNiTi wire were taken in 4 group (1 control group soaked in artificial saliva and 3 treatment groups soaked in avocado seed extract ). Samples were immersed in avocado seed extract with concentrations of 1,5 g/L, 2 g/L and 2,5g/L for 7 days. For surface roughness was test Surface Roughness Average analysis. One way ANOVA test showed that there was a significant difference between the control group and all treatment groups in the surface roughness test with a value of p = 0.000. Post Hoc LSD test showed that there were no significant differences between treatment group 2 and treatment group 3 with a p value = 0.122. Providing avocado seed extract with tannin content at concentrations of 1.5 g/L and 2 g/L can reduce surface roughness on CuNiTi wire due to the corrosion process.
Full Text:
PDFReferences
Eliades T, Athunasial, 2002, In Vivo anging of orthodontic alloy : implication for corrosion potential, nickel release, and biocompatibility. Angle Orthod. Vol.72: 222 – 37.
Gravina, Marco Abdo, Ione Helena Vieira Portella Brunharo, Cristiane Canavarro, Carlos Nelson Elias, dan Cátia Cardoso Abdo Quintão. 2013. Mechanical properties of NiTi and CuNiTi shape-memory wires used in orthodontic treatment. Part 1: Stress-strain tests. Dental Press Journal of Orthodontics 18(4):35–42. doi: 10.1590/S2176- 94512013000400007.
Habar, E.H., Tatengkeng, F., 2020. The difference of corrosion resistance between NiTi archwires and NiTi with additional cooper archwires in artificial saliva. Journal of Dentomaxillofacial Science 5, 120.
Gravina, M.A., Brunharo, I.H.V.P., Canavarro, C., Elias, C.N., Quintão, C.C.A., 2013a. Mechanical properties of NiTi and CuNiTi shape-memory wires used in orthodontic treatment. Part 1: Stress-strain tests. Dental Press Journal of Orthodontics 18, 35–42.
Fatene, N., Mansouri, S., Elkhalfi, B., Berrada, M., Mounaji, K., Soukri, A., 2019. Assessment of the electrochemical behaviour of Nickel-Titanium-based orthodontic wires: Effect of some natural corrosion inhibitors in comparison with fluoride. J Clin Exp Dent 11, 414–434.
Castro, S.M., Ponces, M.J., Lopes, J.D., Vasconcelos, M., Pollmann, M.C.F., 2015. Orthodontic wires and its corrosion - The specific case of stainless steel and beta-titanium. Journal of Dental Sciences.
Sheikh, T., Ghorbani, M., Tahmasbi, S., Yaghoubnejad, Y., 2015. Galvanic Corrosion of Orthodontic Brackets and Wires in Acidic Artificial Saliva: Part II. Journal of Dental School 33, 88–97.
Jura, C.O., Tendean, L.E.N., Anindita, P.S., 2015. Jumlah Ion Kromium (Cr) dan Nikel (Ni) Kawat Ortodontik Stainless Steel yang Terlepas dalam Perendaman Saliva. e-GIGI 3.
Sabane, A.V., Deshmukh, S.V., Sable, R.B., 2009. The Effect of Flouride Prophylactic Agents on the Mechanical Properties and Surface Topography of Orthodontic Arch Wires-An in Vitro Study. Journal of Indian Orthodontic Society 43, 18–24.
Jaber, L.C.L., Rodrigues, J.A., Amaral, F.L.B., França, F.M.G., Basting, R.T., Turssi, C.P., 2014. Degradation of orthodontic wires under simulated cariogenic and erosive conditions. Brazilian oral research 28, 1–6.
H. Al-mashhadani, M., A. Ahmed, A., Hussain, Z., A. Mohammed, S., M. Yusop, R., Yousif, E., 2020. Inhibition of Corrosion: Mechanisms and Classifications in Overview. Al-Qadisiyah Journal Of Pure Science 25, 1–9.
Manongko, P.S., Sangi, M.S., Momuat, L.I., 2020. Uji Senyawa Fitokimia dan Aktivitas Antioksidan Tanaman Patah Tulang (Euphorbia tirucalli L.). Jurnal MIPA 9, 64.
Verti, E.A., Mustikarini, E.D., Lestari, T., 2021. Diversity of Avocado Germplasm (Persea americana) in Bangka Island Based on Morphological Character. Proceeding of National Colloquium Research and Community Service Vol.5, 33–38.
Halimah, N., Aulia, Dewi, Istiqomah, I., Rohmah, S., 2014. Pengolahan Limbah Biji Alpukat untuk Pembuatan Dodol Pati sebagai Alternatif Pengobatan Ginjal. Jurnal Ilmiah Mahasiswa Fakultas Kesehatan Masyarakat Universitas Diponegoro 4, 32–37.
Frešer, F., Hostnik, G., Tošović, J., Bren, U., 2021. Dependence of the Fe(II)-Gallic Acid Coordination Compound Formation Constant on the pH. Foods 2021, Vol. 10, Page 2689 10, 2689.
Sanjaya, I.K.N., Giantari, N.K.M., Widyastuti, M.D., Laksmiani, N.P.L., 2020. Ekstraksi Katekin Dari Biji Alpukat Dengan Variasi Pelarut Menggunakan Metode Maserasi. Jurnal Kimia 14, 1.
Langen, E.N., Rumampuk, J.F., Leman, M.A., 2017. Pengaruh Saliva Buatan dan Belimbing Wuluh (Averrhoa bilimbi L.) Terhadap Kekerasan Resin Komposit Nano Hybrid.
Kaur, S., Kour, K., Singh, P., 2019. Comparative evaluation of the efficacy of Chlorohexidine mouthwash as a supplement to regular tooth brushing. International Journal of Oral Health Dentistry 5, 97–103.
Alavi, S., Ahmadvand, A., 2021. Ions Release Evaluation and Corrosion of Titanium Mini-Implant Surface in Response to Orthokin, Oral B and Chlorhexidine Mouthwashes. Dental research journal 18, 32.
Nardeli, J. V., Fugivara, C.S., Taryba, M., Pinto, E.R.P., Montemor, M.F., Benedetti, A. V., 2019. Tannin: A natural corrosion inhibitor for aluminum alloys. Progress in Organic Coatings 135, 368–381.
Damaryanti, E., Erstyawati, A.D., 2021. EFEKTIVITAS EKSTRAK KULIT BUAH KAKAO ( Theobroma cacao L . ) SEBAGAI INHIBITOR LAJU KOROSI KAWAT STAINLESS STEEL PERANTI ORTODONTI LEPASAN. E-Prodenta Journal of Dentistry 5, 393–402.
Proença, C.S., Serrano, B., Correia, J., Araújo, M.E.M., 2022. Evaluation of Tannins as Potential Green Corrosion Inhibitors of Aluminium Alloy Used in Aeronautical Industry. Metals 12.
Zhang, D., 2022. Saliva: Properties and Functions in Food Oral Processing, in: Oral Processing and Consumer Perception. hal. 342.
Saputri, I.D., Joelijanto, R., Sandra, L., Ade, D., 2015. Daya Inhibisi Korosi Ekstrak Daun Belimbing Wuluh ( Averrhoa bilimbi L . ) terhadap Kawat Thermal NiTi Ortodonti ( Corrosion Inhibition of Starfruit Leaves Extract ( Averrhoa bilimbi L .) on Thermal NiTi Orthodontic Wire ). e-Jurnal Pustaka Kesehatan 3, 199–204.
Mardiah, M., Lapua, E.P., Wahyudiantara, I.P., Iqbal, M., Lestari, I., Rodiyatunnisa, R., Sakinah, N., Novianti, H.L., Fadilah, O.A., 2018. Studi Laju Korosi Logam Aluminium dengan Penambahan Inhibitor dari Ekstrak Daun Karamunting (Rhodomyrtus tomentosa) dalam Larutan NaCl. Jurnal Chemurgy 1, 39.
Taqwa, M.L., Irwan, Pardi, 2021. Penggunaan Ekstrak Daun Pepaya Sebagai Inhibitor Korosi Baja Karbon Dalam Lingkungan Crude Oil. Teknologi 21, 1–6.
Rais, F., Wahyuningtyas, D., 2021. Pengendalian Laju Korosi Baja dengan Penambahan Ekstrak Biji Alpukat sebagai Green Inhibitor. Jurnal Inovasi Proses 6.
Furlan, T.P.R., Barbosa, J.A., Basting, R.T., 2018. Nickel, Copper, and Chromium release by CuNi-titanium Orthodontic Archwires is Dependent on the pH Media. Journal of International Oral Health 10, 224–228.
Sumule, I., Anindita, P.S., Waworuntu, O.A., 2015. Pelepasan Ion Nikel Dan Kromium Braket Stainless Steel Yang Direndam Dalam Minuman Berkarbonasi. e-GIGI 3, 1–6.
Yuliani, H., Rasyid, M.I., 2019. Efek Perbedaan Pelarut terhadap Uji Toksisitas Ekstrak Pineung Nyen Teusalee. Jurnal Fitofarmaka Indonesia 6, 347–352.
Martín-Cameán, A., Jos, Á., Mellado-García, P., Iglesias-Linares, A., Solano, E., Cameán, A.M., 2015. In vitro and in vivo evidence of the cytotoxic and genotoxic effects of metal ions released by orthodontic appliances: A review. Environmental Toxicology and Pharmacology 40, 86–113.
de Albuquerque, C.G., Correr, A.B., Venezian, G.C., Santamaria, M., Tubel, C.A., Vedovello, S.A.S., 2017. Deflection and Flexural Strength Effects on the Roughness of aesthetic-coated orthodontic wires. Brazilian Dental Journal 28, 40–45
Chantarawaratit, P. on, Yanisarapan, T., 2021. Exposure to the oral environment enhances the corrosion of metal orthodontic appliances caused by fluoride-containing products: Cytotoxicity, metal ion release, and surface roughness. American Journal of Orthodontics and Dentofacial Orthopedics 160, 101–112.
DOI: https://doi.org/10.31983/jkg.v11i1.10755
Article Metrics
Refbacks
- There are currently no refbacks.
|  |
|
|
|
|
|
|  |  |  |  |  |  |
| View My Stats |